Studi Karakteristik Marshall Pada Campuran Lapis Aspal Beton (Laston) dengan Bahan Tambah Limbah Kain Nilon
Abstract
The use of nylon fabric waste as adding material for concrete asphalt layers can be one of the solutions, because it can reduce pollution in the environment.The level of variation in adding nylon fabric waste is 0%, 5%, 10% and 15%. Sample testing as many as 24 test specimens. . The purpose of this study is to determine the physical properties of the asphalt with the added material of the nylon fabric waste and to determine the properties of the concrete asphalt layer mixture (Laston) with the added material of the nylon fabric waste. The results of testing the addition of nylon fabric waste levels as added material to the asphalt show that the value of the physical properties of asphalt is penetration, soft point, specific gravity, flame point and fuel point and asphalt dactality meets the standard specifications of the 2018 SNI Marga. As well as the addition of nylon substitution waste a number of asphalt at 5%, 10% and 15% content can affect the nature of concrete asphalt layers (Laston). In variations of 5%, 10% and 15% density value of 2,336 gr/cm, 2,327 gr/cm, 2,343 gr/cm, stability of 1892,4 kg, 2239,0 kg, 1953,6 kg, VMA of 15,9%, 16,2%, 15,6%, VIM of 4,4%, 4,7%, 4,1%, VFB of 73,6%, 70,9%, 74,0%, melting of 3,93 mm, 3,43 mm, 3,02 mm and MQ of 480,1 kg/mm, 652,9 kg/mm, 691,5 kg/mm.
Downloads
References
Bancin, E.D.L., Lubis, K., Mahd, N. 2021. Pengaruh Penggunaan Tanah Merah Sebagai Filler Pada Campuran Aspal Ac-Bc Terhadap Nilai Marshall, Journal of Civil Engineering Building and Transportation, Vol 5 (1). PP:17-25.
Kurniasari, F.D., Saleh, S.M., Sugiato, S. 2018. Pengaruh Filler Abu Ampas Tebu (Aat) Dengan Bahan Pengikat Aspal Pen 60/70 Pada Campuran Laston Ac-Wc, Jurnal Arsip Teknik Sipil dan Perencanaan (JARSP), Universitas Syiah Kuala, Banda Aceh, Vol1 (4). PP: 69- 78.
Nur, N.K., Mahyuddin., Bachtiar, E.,dkk.2021. Perancangan Perkerasan Jalan, Yayasan Kita Menulis, Medan.
Palmer, R. J. 2001. Polyamides, Plastics. Encyclopedia Of Polymer Science and Technology. Putri, L.R., Widiastuti, M., Alkas, M.J. 2022. Pengaruh Penggunaan Crumb Rubber Dengan Material Senoni Dan Filler Batu Senoni Terhadap Nilai Karakteristik Marshall Asphalt Concrete–Binder Course (Ac-Bc), Jurnal Ilmu Pengetahuan dan Teknologi Sipil, Universitas Mulawarman, Vol 6 (1). PP: 21-29.
Saleh, A., Yulistia, E., Rambe, F.R. 2017. Purifikasi Biogas Bedasarkan Perbedaan Mesh Kain Nilon Dan Laju Alir Biogas, Jurnal Teknik Kimia, Universitas Sriwiaya, Vol 2 (2). PP: 137- 145.
Saragi, Y.R., Sinaga, A.J. 2021. Analisis Lapisan Aspal Beton (Ac-Bc) Dengan Penambahan Limbah Kaleng Minuman Ditinjau Dari Karakteristik Marshall Dan Uji Penetrasi, Jurnal Teknik Sipil, Universitas HKBP Nommensen Medan, Vol1 (1). PP: 49-58.
Septiawan, T. D. 2013. Pengaruh Penggunaan Bahan Tambah Serbuk Karet Ban Pada Campuran Lapis Aspal Beton, Jurnal Rekayasa Sipil, Vol 1 (1). PP: 9-17.
Suprayitno., Mudjanarko, S.W. 2019. Studi Analisis Uji Marshall Pada Pembuatan Campuran Aspal Plastik Jenis Hdpe, Jurnal Spirit Pro Patria, Vol5 (2).
Syaharuddin., Hafram, S.M., Alifuddin, A. 2021. Pengaruh Variasi Slag Nikel Sebagai BahanTambah Agregat Halus Pada Campuran Lapisan Aspal Beton, Jurnal Teknik Sipil, Universitas Muslim Indonesia, Vol 6 (2). PP: 101-107.
Widayanti, A., Soemitro, R.A.A., Ekaputri, J.J., Suprayitno, H. 2018. Kinerja Campuran Aspal Beton Dengan Reclaimed Asphalt Pavement Dari Jalan Nasional Di Provinsi JawaTimur, Jurnal Manajemen AsetInfrastruktur dan Fasilitas, Surabaya, Vol 2 (1). PP: 35-43.
Copyright (c) 2023 Yusnianti Yusnianti, Sufrianto Sufrianto, hujiyanto hujiyanto, Syamsuddin Syamsuddin
This work is licensed under a Creative Commons Attribution 4.0 International License.